800 series industrial repair agent

811 iron repair agent two-component, mastic, universal. It is suitable for repairing pores, sand holes and cracks in iron castings. It can be especially used for the repair of finishing mating surface and the recovery of dimensional deviation. Can be machined after curing. 812 steel repair agent two-component, mastic, high comprehensive mechanical properties. High strength, high reliability, suitable for small gap or aperture below all kinds of casting porosity, sand hole, crack repair. It can also be used for wear repair of machine parts and can be machined after curing. 813 aluminum repair agent two-component, mastic, aluminum as a filler polymer aluminum repair material. Suitable for all kinds of aluminum materials and aluminum casting pores, sand

Category:Product Center

Keywords: 800 series industrial repair agent

E-mail: jinhuifirst@163.com

Message Contacts

Product Details

811 iron repair agent Two-component, mastic, universal. It is suitable for repairing pores, sand holes and cracks in iron castings. It can be especially used for the repair of finishing mating surface and the recovery of dimensional deviation. Can be machined after curing.	812 steel repair agent Two-component, mastic, high comprehensive mechanical properties. High strength, high reliability, suitable for small gap or aperture below all kinds of casting porosity, sand hole, crack repair. It can also be used for wear repair of machine parts and can be machined after curing.	813 aluminum repair agent Two-component, mastic, aluminum-based polymeric aluminum repair material. Suitable for all kinds of aluminum materials and aluminum casting pores, sand holes, shrinkage and other defects repair and scratch, crack, wear repair. After curing, it can be machined, and the color is consistent with the main body.
528 oil surface emergency repair agent Two-component, liquid, fast positioning, can be repaired with oil. It is used to repair oil leakage and leakage of transformers, oil tanks, oil tanks, oil pipes, flanges and other equipment (note: not suitable for plugging copper pipelines).	838 Leakage Stopping Steel Bar with Pressure 3~5 minutes curing. After kneading evenly by hand, fill in the gap or hole to plug the leakage. Used for plugging under the working condition of steel material pressure lower than 0.3MPa.	801 conveyor belt fast cold viscose Polyurethane two-component fast curing, high strength, bonding without heating, pressure. Used for cold bonding of multi-layer core rubber conveyor belt joints. Used for rubber-rubber, rubber-metal, rubber-fabric bonding. The initial viscosity is strong, and the load can be run after 30 minutes of viscosity.

Technical performance of industrial repair agent products

Product code	Packing specification	Before curing		After curing
Product code	Packing specification	Viscosity (physical state)	Color	Degreaser (g/cm³)	Shear strength (N/mm2)	Compressive strength (MPa)	Tensile strength (Mpa)	Bending strength (Mpa)	Hardness (Shore D)	Temperature range (℃)
811	500 g/set	Mastic	Iron	1.62	20.5	96.8	32.2	56.5	84	-60～160
812	500 g/set	Mastic	Grey	1.68	22	105.3	37.8	58.3	84	-60～160
813	250 g/set	Mastic	Aluminum	1.41	22.5	99.2	32.6	51.6	82	-60～160
814	250 g/set	Mastic	BRASS	1.53	21	90.6	35.9	51.4	81	-60～160
528	85 g/set	liquid	Colorless	0.94	31.8	90.6	-	67.3	84	-60～120
838	100 g/set	Mastic	Grey	1.82	13.2	95.5	-	32.5	84	-60～149
801	500 g/set	Mastic	light brown	-	-	-	9.0	-	65	-50～120

Product code	Mixing ratio (A:B)		Operation time (200g when mixed) (min)	Before putting into operation (No load, no immersion) Minimum curing time required (h)	Curing time before machining or light load (h)	Curing time before full mechanical load or thermal load operation (h)	Curing time before soaking chemicals (h)
Product code	weight ratio	volume ratio	Operation time (200g when mixed) (min)		Curing time before machining or light load (h)		Curing time before soaking chemicals (h)
811	7：1	4：1	40～60	8	12	24	72
812	7：1	4：1	40～60	8	12	24	72
813	6:1	4.5:1	40～60	8	12	24	72
814	6:1	4：1	40～60	8	12	24	72
528	1:1	1:1	3～5	20	-	6	-
838	Cut as required	3～5	10	-	6	-
801	10:1	-	40	-	2	8	-